YOTEBLE 100g Auto Body Filler with 10gHardener Fast Drying Original Formula — Open-Box, 11% Off

High Adhesion: YOTEBLE body filler for car is specially developed for metal, aluminum and fiberglass surfaces in automobiles and fills scratches and dents with strong adhesion and peel resistance. It is heat resistant and frost resistant (-40C to 140C), crack resistant and bubble resistant. It also offers excellent flexibility and can withstand even slight deformation of the bodywork Durable and Wear-Resistant: The YOTEBLE auto body filler adheres perfectly to surfaces such as steel and aluminium alloys. After curing, it has a dense texture and medium hardness, which makes it easy to grind. The polished edges are smooth and distortion-free, making the repaired area durable and vibration and shockproof Excellent Filling Power: The car paint scratch repair fills dents up to a depth of 5mm. The minimum volume shrinkage during curing effectively prevents the surface from sinking and ensures an evenly smooth repair surface Easy to Use: The car body filler is smooth and spreadable. (Putty: hardener = 100:2) After mixing with the hardener, it dries for 30 minutes. After drying, it can be easily sanded with sandpaper and is therefore easy to use even for beginners Flexible Applicability: The body filler is suitable for body repairs, model making, DIY work, ship scratch repair, paint scratch repair, and other applications with versatile usage options Fast Curing Time: The filler cures quickly at room temperature, typically ready for sanding within 30-35 minutes, which shortens repair cycles and allows for efficient completion of automotive body repair projects

This professional car body filler is designed for body repair and surface treatment. Thanks to its excellent filling properties, it quickly repairs scratches, dents, therefore suit for a variety of surfaces, including steel, aluminium and fibreglass. After curing, it is hard and easy to sand.   This creates a smooth, fine finish that provides an ideal foundation for subsequent painting.

Advantages:

1.SMOOTH APPLICATION Smooth paste allows for easy application and increases job satisfaction.

2. Efficiency: Fast curing shortens repair cycles and speeds up vehicle delivery.

3. LONG LASTING RESULTS Strong adhesion and low shrinkage ensure long term stable repair results and eliminate the need for rework.

4. EASY GRINDING Smooth grinding saves time and effort and provides a flawless finish.

5. Wide Application Suitable for a variety of common metal substrates and meets most repair requirements.

Recommendations for use:

1.   Surface Preparation Make sure the metal surface to be repaired is thoroughly clean and free of oil, moisture and old paint.

2.   Mixing ratio: mix putty and hardener in the exact weight ratio of 100:2.   For best results, always use the included hardener.

3.   Stirring: mix hardener and putty thoroughly and evenly until the colours are completely uniform and streak-free.

4.   Peel: Apply the mixed putty to the repair site with light pressure to ensure close contact with the substrate.   It is recommended to apply the putty slightly above the surrounding intact surface to facilitate sanding.

5.   Curing time: at room temperature (approx.   25 °C) can usually start grinding after 30-35 minutes (the exact time varies according to temperature, humidity and layer thickness, please adjust accordingly).

6.   Sanding: Once the putty is fully cured (hard to the touch), sand it with coarse sandpaper (first with fine sandpaper) until the surface is smooth and level and adapts perfectly to the body contours.

Precautions:

1.   Work in a well-ventilated environment to avoid inhaling dust.   Wearing a protective mask, gloves and goggles is recommended.

2.   Too high a hardener content leads to a rapid reaction and brittle cracking;   too low a proportion leads to incomplete or incomplete curing.   Please strictly adhere to the recommended ratio.

3.   This product is not suitable for plastics, galvanic coatings, galvanized coatings or untreated, rusted surfaces as this can lead to poor adhesion and peeling.